EN BS DIN 42CrMo4 / 42CrMo Alloy Steel Plate Custom Cutting any Size as Request
Products Specification of Steel Plate
| Products Name | 42CrMo4 Alloy Steel Plate |
| Thickness | 10.0 - 200.0mm |
| Width | 100 - 2200mm custom cutting any size as request |
| Length | 6m 8m 10m 11.5m 12m or cutting any length as request |
| Standard | ASTM JIS GB EN |
| MOQ | 500 Kgs |
| Deliver time | 7 - 14 days |
| Loading Port | Shanghai Port |
| Packing | wooden pallets |
| Other Grade | AR400 / AR450 / AR500 / AR600 NM400 NM450 NM500 NM600 |
| Service | Cutting, Heat treatment |
42CrMo4 Alloy Steel – SAE-AISI 4140 is classified as low alloy steel. Medium carbon steels are high-strength steels that include EN19 as an important member in the low alloy category. These steels show a positive response to a variety of heat treatments. 42CrMo4 is a 1% chromium – molybdenum medium hardenability general purpose high tensile steel – generally supplied hardened and tempered in the tensile range of 850 –1000 Mpa (condition T). 42CrMo4 Alloy steel is a high quality, high tensile alloy steel usually supplied readily machinable in ' T' condition, giving good ductility and shock resisting properties combined with resistance to wear. We specialize in the supply of EN19, 4140, 42CrMo4 Hot Rolled Steel Round Bars.
42CRMO4 Grade Application:
42CrMo4 alloy steel is widely used for engineering steel purpose, such as: making various kinds of machinery, automobile, mining spare part, the gearwheel of the engine, the driving gear of supercharger, the connecting rob, the pin chock under the high pressure, parts for power train applications, cold formed fastener components, shafts, gears, drill collars for the oil exploration, etc.
42CRMO4 Equivalent grades:
AISI 4140, SAE 4140, 42CrMo4, 42CrMoS4, Din 1.7225
Addition to other grades:
MS, EN1A, EN3B, EN8, EN8D, EN9, EN24, EN31, EN32B, EN36C, EN41B, EN43B, EN47, EN353, IS2062, 42Crmo4, HCHCR, D2, D3, H-11, H-13, CW-1, OHNS M2, M35, M42, DIN-1.2714, P20, P20+S, P20+Ni, SCM420, ASTMSA-36, ASTM SA-105 , SAE1018, SAE1010, SAE4140, SAE8620, 16MNCR5, 20MNCR5, C20, C45, C50, C60, CK45, 20C8, 40C8, 45C8, 55C8, C55MN75, SAE52100, S40C, S355J2G3.
42CRMO4 Chemical composition:
The following table shows the chemical composition of 42CRMo4 steel:
Element | C | Si | Mn | P | S | Cr | Mo |
Content(%) | 0.38-0.45 | 0.40 max | 0.60-0.90 | 0.035 max | 0.035 max | 0.90-1.20 | 0.15-0.30 |
42CRMO4 Mechanical Properties:
Size Ø mm | Yield stress Rp0.2,N/nn2, min | Ultimate tensile Stress, Rm,N/nn2 | Elongation A5,%, min | Hardness HB | Toughness KV, Joule, min. |
<40 | 750 | 1000-1200 | 11 | 295-355 | 35 at 20 °C |
40-95 | 650 | 900-1100 | 12 | 265-325 | 35 at 20 °C |
>95 | 550 | 800-950 | 13 | 235-295 | 35 at 20 °C |
42CRMO4 Hardness:
295 – 355
42CRMO4 Heat treatment:
42CrMo4 is alloy steel for quenching and tempering, which has a good combination of strength and toughness in the quenched and tempered condition. After the oil quenching, the steel will be hardened up to ø60 mm bar diameter. The microstructure of larger dimensions is not a fully martensite.
42CRMO4 Hardening:
First quenching heated slowly to 880°C, Then after adequate soaking at this temperature quench in oil or water. Temper as soon as tools reach room temperature. Second quenching heat to 780-820°C, then quenching in oil or water.
42CRMO4 Tempering:
Heat to 205-649°C, then cools in water or oil. normal delivery hardness 18-22 HRC.
42CRMO4 Physical Properties:
Quantity | Value | Unit |
Thermal expansion | 10 – 10 | e-6/K |
Thermal conductivity | 25 – 25 | W/m.K |
Specific heat | 460 – 460 | J/kg.K |
Melting temperature | 1450 – 1450 | °C |
Density | 7700 – 7700 | kg/m3 |
Resistivity | 0.55 – 0.55 | Ohm.mm2/m |
42CRMO4 Thermal Properties:Thermal conductivity: 0,42 kW/(cm*K)
42CRMO4 Forging Properties:42CrMo4 is forged at 926 to 1205°C.
42CRMO4 Stress Relieving:450-650°C
42CRMO4 Normalizing:840-880 °C
42CRMO4 Annealing:
-
Heat steel 42CrMo4 forged steel slowly and thoroughly to 800-850°C;
-
Cool slowly in the furnace to the temperature 480°C;
-
Complete annealing the steel in the air.
42CRMO4 Density:7.85kg/m3
Tensile strength: 655 MPA
42CRMO4 Machinability:42CrMo4 alloy steel has good machinability in the annealed condition.
42CRMO4 Welding:
Engineering steel 42CrMo4 has only limited weldability. Preheating to 200-300°C is strongly recommended; the upper limit should not be exceeded because of the risk for deterioration of the chrome layer. Alloy steel 42CrMo4 can be friction welded. However, precautions are necessary so as to limit the formation of undesirable microstructures in the welded zone.