P355GH Hot Rolled Steel Plate / Pressure Vessel Plate 1500*6000mm 2000*8000mm
| Product Name | Q345R / P355GH Steel Plate |
| Thickness | 3mm~300mm,2mm-100mm is common thickness,also can customize |
| Width | 1000~3000mm,common width is 1250mm,1500mm,2000mm,2200mm |
| Length | 1000~12000mm,can as your request cut |
| Surface | Clean,finished, blasting and painting or as your request |
| Delivery | Hot Rolled, Controlled Rolling,Normalizing,Annealing, Tempering,Quanching, Q+T |
| Packing | Steel Strapping,fixing in the Container,can customize |
| Thickness tolerance | ±0.3mm |
| Application | It is mainly used to make structural parts such as car girder, beam, transmission shaft and car chassis parts, which can reduce the weight of the parts. |
Product Introduction
P355GH is a pressure vessel steel grade as specified under the Euro Norm standard (EN10028) which has superseded British Standard and DIN standard equivalents.
This normalized steel is used worldwide by fabricators of welded pressure vessels, industrial boilers and heat exchangers and is engineered to work well in elevated temperature service.
Properties
Steels for pressure vessels and boilers differ from other carbon-manganese structural steels due to their high resistance to pressure at all temperatures (ambient, low or high).
Advantages
The fundamental property of steels for pressure vessels is their ability to withstand high pressure at different temperatures. They have good weldability, as well as excellent toughness, and are suitable for normalization annealing and stress-relief annealing (both treatments neutralize local hardening caused by welding).
Applications
Steels for pressure vessels are mainly used to manufacture boilers, drums, pressure or steam piping, industrial thermal vessels and heat exchangers. These steels are suitable for mechanical forming and welding.
Technical Data
Chemical Composition of EN 10028 – P355GH
| Element | % by mass | Element | % by mass |
| Carbon (C) | ≤0.16 | Silicon (Si) | ≤0.35 |
| Manganese (Mn) | 0.60 to 1.20 | Phosphorous (P) (max) | 0.025 |
| Sulphur (S) (max) | 0.015 | Aluminium (Al) | ≤0.020 |
| Nitrogen (N) | ≤0.012 | Chromium (Cr) | ≤0.30 |
| Copper (Cu) | ≤0.30 | Molybdenum (Mo) | ≤0.08 |
| Niobium (Nb) | ≤0.020 | Nickel (Ni) | ≤0.30 |
| Titanium (Ti) (max) | 0.03 | Vanadium (Vi) | ≤0.02 |
Mechanical Properties of EN 10028 – P355GH
| Type | Thickness (mm) | Yield Strength
MPa (min) | Tensile Strength
MPa | Elongation
% (min) | Impact Energy
(KV J) (min) |
| -20° | 0° | +20° |
| Normalized | ≤ 16 | 355 | 510 – 650 | 21 | 27 | 34 | 40 |
| 16> to ≤40 | 345 | 510 – 650 | 21 | 27 | 34 | 40 |
| 40> to ≤60 | 335 | 460 – 580 | 21 | 27 | 34 | 40 |
| 60> to ≤100 | 315 | 490 – 630 | 21 | 27 | 34 | 40 |
| 100>to≤150 | 295 | 480 – 630 | 21 | 27 | 34 | 40 |
| 150>to≤250 | 280 | 470 – 630 | 21 | 27 | 34 | 40 |
| Equivalent Steel Grade of P355GH |
| Europe | Belgium | Germany | France | Italy | Sweden | India | Japan |
| Fe E355 | D52-1,2 | 19Mn8 | A52 CP | Fe510-1-KW | SS 21,06,01 | – | SPV355 |
|
|
P355GH Hot Rolled Steel Plate / Pressure Vessel Plate 1500*6000mm 2000*8000mm Images
|